Semi-Oxidized Bitumen 80/100
Which is a new grade of Bitumen that our company has started producing recently
| TEST |
METHOD |
SPECIFICATION |
| Density @ 15°C kg/l |
ASTM D - 70 |
-- |
| Penetration @ 25°C (100 gm, 5 Sec.) 1/10 mm |
ASTM D - 5 |
80 - 100 |
| Softening Point by Ring and Ball Method °C |
ASTM D - 36 |
42 - 52 |
| Ductility @ 25°C ( 5 Cm / Min ) Cm |
ASTM D - 113 |
Min. 100 |
| Flash Point ( Cleveland Open Cup ) °C |
ASTM D - 92 |
Min. 200 |
| Solubility in Trichloro Ethylene % mass |
ASTM D - 2042 |
Min. 99 |
| Thin Film Oven Test, (3.2mm) @ 163°C, 5hrs : |
ASTM D - 1754 |
-- |
| Loss on heating % mass |
-- |
Max. 1 |
| Penetration of Residue @ 25 °C % of Original |
-- |
Min. 47 |
| Ductility of Residue @ 25 °C ( 5Cm / Min ) Cm |
-- |
Min. 75 |
| Paraffin wax content |
Din - 52015 |
-- |
| Loss of Heating % mass |
ASTM - D6 |
-- |
Uses of ( Oxidized ) Bitumen :
- Fillin spaces in the concrate.
- Protecting pipes from corrosion.
- Cables industry.
- Pavement of the street.
- First quantity is taken by ASPC in 17 March 2019
- The quantity is 46.420 ton
Oxidized Bitumen 60/70 Heavy Duty for Exportation
| TEST |
METHOD |
SPECIFICATION |
| Relative Density @ 25 / 25 °C |
ASTM D - 70 |
Reported |
| Penetration @ 25°C (100 gm, 5 Sec.) 1/10 mm |
ASTM D - 5 |
60 - 70 |
| Softening Point by Ring and Ball Method °C |
ASTM D - 36 |
Min. 48 |
| Ductility @ 25°C ( 5 Cm / Min ) Cm |
ASTM D - 113 |
Min. 100 |
| Flash Point ( Cleveland Open Cup ) °C |
ASTM D - 92 |
Min. 250 |
| Viscosity kinematic @ 135 °C cSt |
ASTM D - 2170 |
Min. 320 |
| Solubility in Trichloro Ethylene % mass |
ASTM D - 2024 |
Min. 99.5 |
| Thin Film Oven Test, (3.2mm) @ 163°C, 5hrs : |
ASTM D - 1754 |
-- |
| Loss on heating % mass |
-- |
Max. 1 |
| Penetration of Residue @ 25 °C % of Original |
-- |
Min. 52 |
| Ductility of Residue @ 25 °C ( 5Cm / Min ) Cm |
-- |
Min. 50 |
Oxidized Bitumen (Grade 95/25) for Exportation
| TEST |
METHOD |
SPECIFICATION |
| Penetration @ 25°C (100 gm, 5 Sec.) 1/10 mm |
ASTM D - 5 |
20 / 30 |
| Softening Point ( Ring and Ball ) °C |
ASTM D - 36 |
90 / 100 |
| Ductility @ 25°C Cm |
ASTM D - 113 |
Min. 1.0 |
| Flash Point ( Cleveland Open Cup ) °C |
ASTM D - 92 |
Min. 200 |
| Solubility in Trichloro Ethylene % mass |
ASTM D - 2024 |
Min. 99 |
| Loss on heating @ 163°C, 5hrs % mass |
ASTM D - 6 |
Max. 0.2 |
Bitumen Packing in pallets:
- Weight of pallet is about 500 ~ 600 kg
- It has 24 Block
- Block has 25 kg
- Block 9 Sheets
- Sheet 40 cm * 80 cm * 7.5 mm
Uses of ( Oxidized ) Bitumen :
- Fillin spaces in the concrate.
- Protecting pipes from corrosion.
- Insulating material.
- Battery industry.
- Cables industry.
- Stiking material in refregeration rooms.